English
Description :
DENEPOX™ 40 is an ultra low viscosity, 2 components epoxy injection resin for structural injections in concrete in both dry and wet environments.
Technical Information :
| Property |
Value |
Norm |
| Bonding strength on dry concrete |
Exceeds coherence of concrete |
ISO 4624 |
| Bonding strength on damp concrete |
Exceeds coherence of concrete |
ISO 4624 |
| Compressive strength |
Approx. 100N/mm² |
NBN EM 196 |
| Tensile strength |
> 50 N/mm² |
|
| Bending strength |
> 60 N/mm |
NBN EM 196 |
| Elongation at break |
< 10% |
|
| Glass transition temperature |
< 60°C |
EN 12614 |
| Density |
1-1.1kg/dm³ |
|
| Viscosity (mixture) at 25°C |
Approx. 85 |
Test DNC |
| Pot life |
Approx. 80 minutes (100 g at 25°C) |
Test DNC |
| Minimum application temperature |
Approx. 10°C |
|
Full chemical or mechanical resistances are only reached after a curing period of 7 days at 20°C. Mechanical properties of epoxy resins decrease at temperatures higher than 50°C.
Packing : 3kg pail comprising - Part A : 2.3kg, Part B : 0.7kg in metal pails.
华语
简介 :DENEPOX™40是一种超低粘度的双组分环氧树脂注射灌浆，用在干燥和潮湿环境中的混凝土结构注射。
技术资料：
| 项目 |
值 |
测试标准 |
| 干混凝土粘结强度 |
超过混凝土的附著性 |
ISO 4624 |
| 湿混凝土粘结强度 |
超过混凝土的附著性 |
ISO 4624 |
| 抗压强度 |
~100N/mm² |
NBN EM 196 |
| 抗拉强度 |
> 50 N/mm² |
|
| 抗弯强度 |
> 60 N/mm |
NBN EM 196 |
| 断裂伸长率 |
< 10% |
|
| 玻璃化转变温度 |
< 60°C |
EN 12614 |
| 密度 |
1-1.1kg/dm³ |
|
| 粘度(混合物) @ 25°C |
~ 85 |
DNC测试 |
| 使用时限 |
~ 80 分钟 (100 克@ 25°C) |
DNC测试 |
| 最低使用温度 |
~ 10°C |
|
在20℃下7天的固化时间后，才能达到完整的抗化学或抗机械性能。环氧树脂的机械性能在高于50℃的温度下会降低。
包装：3公斤配套，包含A组分：2.3公斤， B组分：0.7公斤。
Melayu
Penerangan :DENEPOX ™ 40 adalah jenis grout suntikan epoksi 2 komponen dengan kelikatan ultra rendah untuk suntikan struktur konkrit dalam keadaan kering dan basah.
Informasi Teknikal :
| Ciri-ciri |
Nilai |
Kaedah Ujian |
| Kekuatan lekatan pada konkrit kering |
Melebihi kepaduan konkrit |
ISO 4624 |
| Kekuatan lekatan pada konkrit basah |
Melebihi kepaduan konkrit |
ISO 4624 |
| Kekuatan mampatan |
~ 100N/mm² |
NBN EM 196 |
| Kekuatan tegangan |
> 50 N/mm² |
|
| Kekuatan lenturan |
> 60 N/mm |
NBN EM 196 |
| Pemanjangan takat putus |
< 10% |
|
| Suhu peralihan kaca |
< 60°C |
EN 12614 |
| Ketumpatan |
1-1.1kg/dm³ |
|
| Kelikatan (campuran) @ 25°C |
~ 85 |
Ujian DNC |
| Masa penggunaan |
~ 80 min (100 g @ 25°C) |
Ujian DNC |
| Suhu penggunaan minimum |
~ 10°C |
|
Ketahanan bahan kimia atau mekanikal yang lengkap hanya dicapai selepas tempoh pengesetan 7 hari pada 20°C. Sifat-sifat mekanikal resin epoksi menurun apabila suhu melebihi 50°C.
Pembungkusan : 3kg baldi terdiri daripdada Bahagian A: 2.3kg, Bahagian B: 0.7kg dalam baldi logam.
Vietnamese
Under Construction